CHEMICAL COMPOSITION PERCENTAGE |
||||||||||||
COMMERCIAL DESIGNATION | Cu | Pb | Ni | Fe | Mn | Sn | Si | Al | As | Zn | Sb | P |
OT-Z CB771S Bi-Refined brass alloy ingots dezincification resistance LOW LEAD- UNI EN 1982:2017 approved UBA LIST | 62-65 | 0.2 max | 0.2 max | 0.2 max | 0.1 max | 0.3 max | 0.02 max | 0.45-0.7 | 0.02-0.04 | Resto | 0.04-0.12 |
PHYSICAL AND MECHANICAL |
||||||||||||
COMMERCIAL DESIGNATION | Bulk Density Kg/dm3 | Electrical Conductivity IACS | WorkabilityTtool % Over Bar OT | Linear Shrinkage % | Optimal Casting Range°C | Melting Point inf. (Solidus ) °C | Tensile Strength Rm N/mm2 | Unified Proof Strength Load 0.2% Rp 0.2 N/mm2 | Elongation at Break A % | Brinell Hardness HB | ||
OT-Z CB771S Bi-Refined brass alloy ingots dezincification resistance LOW LEAD- UNI EN 1982:2017 approved UBA LIST | 8.4 | 22 | 70 | 1.8-1.9 | 960-1040 | 880 | 310 min | 130 min | 5 min | 70 min |