CHEMICAL COMPOSITION PERCENTAGE |
||||||||||||
| COMMERCIAL DESIGNATION | Cu | Pb | Ni | Fe | Mn | Sn | Si | Al | As | Zn | Sb | P |
| LEGA Biaffinata OT-B UNI EN 1982:2017 – CB757S approvata LISTA UBA | 58 – 62.5 | 0.2-1.4 | 0.2 | 0.3 | 0.05 | 0.5 | 0.05 | 0.3-0.9 | Resto | : | ||
|
PHYSICAL AND MECHANICAL |
|||||||||||
| COMMERCIAL DESIGNATION | Bulk Density Kg/dm3 | Electrical Conductivity IACS | WorkabilityTtool % Over Bar OT | Linear Shrinkage % | Optimal Casting Range°C | Melting Point inf. (Solidus ) °C | Tensile Strength Rm N/mm2 | Unified Proof Strength Load 0.2% Rp 0.2 N/mm2 | Elongation at Break A % | Brinell Hardness HB | |
| LEGA Biaffinata OT-B UNI EN 1982:2017 – CB757S approvata LISTA UBA | 8.4 | 21 | 80 | 1.9-2 | 980-1080 | 890 | 350 min | 180 min | 13 min | 90 min | |